AU  -  Umer Sajjad, M. Neaz Sheikh, and Muhammad N. S. Hadi
TI  - Use of Graphene in Ambient-Cured Slag-Fly Ash-Based Geopolymer Concrete
SN  - 0889-325x
KW  - Absorption
KW  - Chemical Resistance
KW  - Chloride
KW  - Geopolymer Concrete
N2  - The durability performance of geopolymer concrete against severe environmental conditions is important for implementing geopolymer binders as alternatives to ordinary portland cement (OPC). In this experimental investigation, the impact of adding graphene on the durability characteristics of geopolymer concrete was examined. Graphene was added at 0.5% by weight of aluminosilicate precursors in geopolymer concrete. Permeability, salt ponding, capillary sorptivity, and immersion in chemical agents were performed to assess the durability characteristics of geopolymer concrete without and with graphene, which were also compared with the durability characteristics of OPC concrete without and with graphene. It was found that the addition of graphene in geopolymer concrete reduced the permeable voids by 12% and water absorption by 9%, and improved the resistance against chloride penetration and sulfuric acid exposure. The compressive strength of geopolymer concrete increased by 20% with the addition of graphene. Also, an approximately 70% reduction in the initial and final rate of water absorption was observed in geopolymer concrete with the addition of graphene.
UR  - https://www.concrete.org/publications/internationalconcreteabstractsportal.aspx?m=details&id=51738683
ER  -